Lutene® LB5000

Low Density Polyethylene

LG Chem Ltd.

产品说明：

LUTENE LB5000 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB5000 is also noted for the excellent heat stability and has good silicone coating processibility. LB5000 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB5000 contains no additives.
Agency Ratings:
USA FDA 21CRF 117.1520(c)
Japaness Ministry of Health and Welfare Notification No. 20 Standard
Applications:
Flexible package (Tie layer or sealant layer of laminating film)
Paper and paperboard coating (Release paper, paper cup, kraft paper)

物性信息：

基本信息
特性	可加工性，良好 良好粘结性 内缩量低 无添加剂
用途	层压板 涂层应用 小袋 - 软包装 纸张涂料
加工方法	层压法 挤出涂层

物理性能	额定值	单位制	测试方法
密度	0.918	g/cm3	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	5.0	g/10 min	ASTM D1238

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	43		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 模压成型	8.83	MPa	ASTM D638
断裂, 模压成型	11.8	MPa	ASTM D638
伸长率 (断裂, 模压成型)	550	%	ASTM D638
弯曲模量 (模压成型)	196	MPa	ASTM D790

薄膜	额定值	单位制	测试方法
始封温度 1	110	°C
水蒸气透过性	20	g/m2/24 hr	内部方法

热性能	额定值	单位制	测试方法
维卡软化温度	83.0	°C	ASTM D1525
熔融温度	107	°C	DSC

补充信息	额定值	单位制	测试方法
Adhesion to Aluminum 2	392.3	N/m	内部方法

挤出	额定值	单位制	测试方法
内缩量 3	20.0	mm	内部方法
最小涂层重量 4	13	g/m2	内部方法

备注
1 .	Kraft paper, 40 g/m2
2 .	Coating weight: 40 g/m2(actually aluminum)
3 .	Coating speed: 200 m/min
4 .	Coating speed: 250 m/min