UNITHENE® LH523

High Density Polyethylene

USI Corporation

产品说明：

UNITHENE LH523 is a high density polyethylene (HDPE) especially developed for injection molding. In addition, it can be applied to powder coating after grinding.
High melt index of UNITHENE LH523 makes it exhibit excellent processability. Also, UNITHENE LH523 possesses superb impact strength and resistance to stress crack owing to its lower density.
LH523 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. The products of LH523 can be easily printed after flame, chemical or electronic surface treatment.

物性信息：

基本信息
特性	高 ESCR（抗应力开裂） 高密度 抗撞击性，高 可加工性，良好
用途	涂层应用
加工方法	涂层 注射成型

物理性能	额定值	单位制	测试方法
密度	0.956	g/cm3	ASTM D792
熔流率（熔体流动速率）	23	g/10 min	ASTM D1238

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	68		ASTM D2240

机械性能	额定值	单位制	测试方法
拉伸模量 - 1% 正割 (模压成型)	745	MPa	ASTM D638
抗张强度			ASTM D638
屈服	22.6	MPa	ASTM D638
断裂	28.4	MPa	ASTM D638
伸长率 (断裂)	300	%	ASTM D638
明显的弯曲模量	804	MPa	ASTM D747

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度	34	J/m	ASTM D256

热性能	额定值	单位制	测试方法
脆化温度	< -76.0	°C	ASTM D746
维卡软化温度	125	°C	ASTM D1525
熔融峰值温度	132	°C	ASTM D3418

补充信息
Torsional Stiffness, ASTM D1043: 9200 kg/cm2