Elvax 型号 |
熔融指数 |
%VA含量 |
拉伸强度 Mpa(ASTM D 17083) |
断裂伸长率,%(ASTM D 17083) |
|
Elvax 40 W |
52 |
40 |
5.2-6.2 |
1000-1300 |
|
Elvax 40 L |
3 |
40 |
11 |
1270 |
|
Elvax 140 W |
400 |
33 |
1.7-3.1 |
800-1000 |
|
Elvax 150 W |
43 |
32 |
6.9-8.3 |
900-1100 |
|
Elvax 170 |
0.8 |
35 |
11 |
1400 |
|
Elvax 200 W |
2500 |
28 |
1.6 |
90 |
|
Elvax 205 W |
800 |
28 |
2.6 |
400-600 |
|
Elvax 210 W |
400 |
28 |
2.8 |
800-1000 |
|
Elvax 220 W |
150 |
28 |
5.5 |
800-1000 |
|
Elvax 240 W |
43 |
28 |
9.7 |
800-1000 |
|
Elvax 250 W |
25 |
28 |
11 |
800-1000 |
|
Elvax 260 |
6 |
28 |
24 |
800-1000 |
|
Elvax 265 |
3 |
28 |
29 |
800-1000 |
|
Elvax 310 |
400 |
25 |
3.3 |
800-1000 |
|
Elvax 350 |
19 |
25 |
14 |
800-1000 |
|
Elvax 360 |
2 |
25 |
26 |
800-1000 |
|
Elvax 410 |
500 |
18 |
4.7 |
600-900 |
|
Elvax 420 |
150 |
18 |
8.6 |
600-900 |
|
Elvax 450 |
8 |
18 |
18 |
600-900 |
|
Elvax 460 |
2.5 |
18 |
23 |
600-900 |
|
Elvax 470 |
0.7 |
18 |
26 |
600-900 |
|
Elvax 500 W |
2500 |
14 |
5 |
90 |
|
Elvax 550 |
8 |
15 |
18 |
800-900 |
|
Elvax 560 |
2.5 |
15 |
22 |
800-900 |
|
Elvax 650Q |
8 |
12 |
17 |
750-850 |
|
Elvax 660 |
2.5 |
12 |
21 |
750-850 |
|
Elvax 670 |
0.35 |
12 |
26 |
750-850 |
|
Elvax 750 |
7 |
9 |
15 |
600-750 |
|
Elvax 760 |
2 |
9.3 |
21 |
600-750 |
|
Elvax 770 |
0.8 |
9.5 |
22 |
600-750 |
|
Elvax 880 |
1.2 |
7.5 |
21 |
600-750 |
EVA广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
1、乙酸乙烯含量在5%以下的EVA，其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等；
2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；
3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；
EVA是由LLDPE（线性低密度聚乙烯）和醋酸（VA）共聚而成。
乙烯-醋酸乙烯共聚物，简称EVA。一般醋酸乙烯（VA）的含量在5%-40%，与聚乙烯（PE)相比，EVA由于在分子链中引入醋酸乙烯单体，从而降低了高结晶度，提高了韧性、抗冲击性、填料相溶性和热密封性能，被广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域.