Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| 公司名称: 东莞市东硕塑胶原料有限公司 |
| 联系: 刘小姐 87701584 |
| 地址: 东莞市樟木头塑料市场一期Z栋2号 |
|
|
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 |
| 吸水率 | 0.070 % | 0.070 % | ISO 62 |
| 平衡吸湿 | 0.070 % | 0.070 % | 23°C/50% R.H.; ISO 62 |
| 线性成型收缩率 | 0.0065 cm/cm | 0.0065 in/in | ASTM Data; MD |
| 熔体流动速率 |
11 g/10 min
@Load 5.00 kg, Temperature 200 °C
|
11 g/10 min
@Load 11.0 lb, Temperature 392 °F
|
ASTM Test |
|
12 g/10 min
@Load 5.00 kg, Temperature 200 °C
|
12 g/10 min
@Load 11.0 lb, Temperature 392 °F
|
ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 68 | 68 | ASTM Test |
| 抗张强度(屈服) | 28.3 MPa | 4100 psi | 2 in/min; ASTM Test |
| 32.0 MPa | 4640 psi | 50mm/min; ISO 527 | |
| 伸长率 (断裂) | 40 % | 40 % | 50mm/min, Nominal strain; ISO 527 |
| 100 % | 100 % | 2 in/min; ASTM Test | |
| 100 % | 100 % | 0.2 in/min; ASTM Test | |
| 屈服伸长率 | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| 拉伸模量 | 1.60 GPa | 232 ksi | 1mm/min; ISO 527 |
| 1.72 GPa | 249 ksi | 2 in/min; ASTM Test | |
| 弯曲强度 | 31.0 MPa | 4500 psi | ASTM Test |
| 45.0 MPa | 6530 psi | ISO Data | |
| 弯曲模量 | 1.48 GPa | 215 ksi | ASTM Test |
| 1.75 GPa | 254 ksi | ISO Data | |
| 悬壁梁缺口冲击强度 |
0.270 J/cm
@Thickness 3.17 mm
|
0.506 ft-lb/in
@Thickness 0.125 in
|
ASTM Test |
| 3.50 kJ/m2 | 1.67 ft-lb/in2 | ISO Test | |
| 简支梁无缺口冲击强度 | 10.0 J/cm2 | 47.6 ft-lb/in2 | ISO 179 |
|
3.00 J/cm2
@Temperature -30.0 °C
|
14.3 ft-lb/in2
@Temperature -22.0 °F
|
ISO 179 | |
| 简支梁缺口冲击强度 | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179 |
| 落锤总能量 | 5.00 J | 3.69 ft-lb | ASTM Test |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| 介电常数 |
2.5
@Frequency 1e+9 Hz
|
2.5
@Frequency 1e+9 Hz
|
ASTM Data |
|
2.5
@Frequency 1.00e+6 Hz
|
2.5
@Frequency 1.00e+6 Hz
|
ASTM Data | |
|
2.5
@Frequency 100 Hz
|
2.5
@Frequency 100 Hz
|
IEC 60250 | |
|
2.5
@Frequency 1.00e+6 Hz
|
2.5
@Frequency 1.00e+6 Hz
|
IEC 60250 | |
| 介电强度 | 140 kV/mm | 3560 kV/in | IEC 60243-1 |
| 耗散因数 |
0.00030
@Frequency 1e+9 Hz
|
0.00030
@Frequency 1e+9 Hz
|
ASTM Data |
|
0.00080
@Frequency 1.00e+6 Hz
|
0.00080
@Frequency 1.00e+6 Hz
|
ASTM Data | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 75.0 μm/m-°C | 41.7 μin/in-°F | ISO 11359 |
| 线性热膨胀系数,横向流动 | 72.0 μm/m-°C | 40.0 μin/in-°F | ASTM Test |
| 载荷下热变形温度(0.46 MPa) | 77.0 °C | 171 °F | ISO 75 |
| 82.0 °C | 180 °F | ASTM Test | |
| 载荷下热变形温度(1.8 MPa) | 63.0 °C | 145 °F | ISO 75 |
| 66.0 °C | 151 °F | ASTM Test | |
| 维卡软化温度 | 56.0 °C | 133 °F | (50 °C/h / 50N) - B/50; ISO 306 |
| 91.0 °C | 196 °F | Rate "B" Loading 1 (120 degC/h 10N); ASTM Test | |
| 可燃性(UL94) |
HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
|
HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.573 | 1.573 | ASTM Test |
| 雾度 |
0.21 %
@Thickness 3.20 mm
|
0.21 %
@Thickness 0.126 in
|
ASTM Test |
| Transmission, Visible | 92 % | 92 % |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 190 - 230 °C | 374 - 446 °F | Extrusion |
| 180 - 250 °C | 356 - 482 °F | Injection Molding | |
| 230 °C | 446 °F | Injection molding | |
| 模具温度 | 30.0 - 50.0 °C | 86.0 - 122 °F | Injection Molding |
| 射速 | 50.0 mm/sec | 1.97 in/sec | Injection molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | Clear | |
| 商业地位 | Active America | |
| FDA | Yes | |
| 形式 | Yes | |
| Impact Modified | Yes | |
| NSF Std. 51 | No | |
| NSF Std. 61 | No | |
| Primary Processing Technique | Injection Molding | |
| 加工 | Film Extrusion | |
| Injection Molding | ||
| UL.UL-C | No |