Styrolux® 3G55
丁苯嵌段共聚物
产品说明：
Styrolux® 3G55 is a clear styrene butadiene copolymer (SBC) used mainly in sheet extrusion and thermoforming applications. It is specifically designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of toughness, transparency and economics. Because of the tendency of blocking, 3G55 is mainly used in inline thermoforming. 3G55 is difficult to print and decorate since it contains a microcrystalline wax.
会员资料
|
公司名称: 东莞市东硕塑胶原料有限公司
|
|
联系: 刘小姐 87701584
|
|
地址: 东莞市樟木头塑料市场一期Z栋2号
|
|
Styrolux® 3G55 物性表
|
基本信息
|
|
|
特性
|
-
Block Copolymer
-
超高韧性
-
清晰度，高
|
|
用途
|
|
|
外观
|
|
|
形式
|
|
|
加工方法
|
|
|
物理性能
|
额定值
|
单位制
|
测试方法
|
|
比重
|
1.01
|
g/cm3
|
ASTM D792, ISO 1183
|
|
熔流率（熔体流动速率） (200°C/5.0 kg)
|
13
|
g/10 min
|
ASTM D1238
|
|
溶化体积流率（MVR） (200°C/5.0 kg)
|
14.0
|
cm3/10min
|
ISO 1133
|
|
收缩率
|
|
|
|
|
流动
|
0.65
|
%
|
ASTM D955
|
|
--
|
0.30 到 1.0
|
%
|
ISO 294-4
|
|
吸水率 (饱和, 23°C)
|
0.070
|
%
|
ASTM D570, ISO 62
|
|
硬度
|
额定值
|
单位制
|
测试方法
|
|
肖氏硬度
|
|
|
ISO 868
|
|
邵氏 A
|
97
|
|
ISO 868
|
|
邵氏 D
|
58
|
|
ISO 868
|
|
机械性能
|
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|
|
|
|
--
|
1170
|
MPa
|
ASTM D638
|
|
--
|
900
|
MPa
|
ISO 527-2
|
|
抗张强度
|
|
|
|
|
屈服, 23°C
|
16.0
|
MPa
|
ASTM D638
|
|
屈服, 23°C
|
15.0
|
MPa
|
ISO 527-2
|
|
拉伸应变
|
|
|
|
|
屈服, 23°C
|
2.0
|
%
|
ISO 527-2
|
|
断裂, 23°C
|
> 300
|
%
|
ASTM D638
|
|
标称拉伸断裂应变 (23°C)
|
> 300
|
%
|
ISO 527-2
|
|
弯曲模量
|
|
|
|
|
--
|
758
|
MPa
|
ASTM D790
|
|
--
|
900
|
MPa
|
ISO 178
|
|
弯曲强度
|
|
|
|
|
--
|
17.0
|
MPa
|
ASTM D790
|
|
5.0% 应变
|
18.0
|
MPa
|
|
|
--
|
18.0
|
MPa
|
ISO 178
|
|
薄膜
|
额定值
|
单位制
|
测试方法
|
|
弹性模量 - MD
|
834
|
MPa
|
ASTM D882
|
|
弹性模量 - TD
|
685
|
MPa
|
ASTM D882
|
|
伸长率
|
|
|
ASTM D882
|
|
MD : 断裂
|
310
|
%
|
ASTM D882
|
|
TD : 断裂
|
350
|
%
|
ASTM D882
|
|
埃尔曼多夫抗撕强度
|
|
|
ASTM D1922
|
|
MD
|
830
|
g
|
ASTM D1922
|
|
TD
|
340
|
g
|
ASTM D1922
|
|
氧气传输速率 (23°C, 0% RH)
|
120000
|
cm3/m2/24 hr
|
ASTM D3985
|
|
水气透过率 1(23°C)
|
410
|
g/m2/24 hr
|
ASTM F1249
|
|
冲击性能
|
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 (23°C)
|
85
|
kJ/m2
|
ISO 179
|
|
简支梁无缺口冲击强度 (23°C)
|
无断裂
|
|
ISO 179
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
23°C
|
无断裂
|
|
ASTM D256
|
|
-30°C
|
4.0
|
kJ/m2
|
ISO 180/A
|
|
23°C
|
5.0
|
kJ/m2
|
ISO 180/A
|
|
装有测量仪表的落镖冲击
|
|
|
ASTM D3763
|
|
Peak force
|
10.0
|
J
|
ASTM D3763
|
|
Total energy
|
21.1
|
J
|
ASTM D3763
|
|
热性能
|
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|
|
|
|
0.45 MPa, 未退火
|
66.7
|
°C
|
ASTM D648
|
|
0.45 MPa, 退火
|
62.0
|
°C
|
ISO 75-2/B
|
|
1.8 MPa, 未退火
|
45.6
|
°C
|
ASTM D648
|
|
1.8 MPa, 退火
|
51.0
|
°C
|
ISO 75-2/A
|
|
维卡软化温度
|
|
|
|
|
--
|
71.7
|
°C
|
ASTM D1525 2
|
|
--
|
67.0
|
°C
|
ISO 306/A50
|
|
--
|
35.0
|
°C
|
ISO 306/B50
|
|
线形热膨胀系数 - 流动
|
|
|
|
|
--
|
1.3E-4
|
cm/cm/°C
|
ASTM D696
|
|
--
|
6.0E-5 到 9.0E-5
|
cm/cm/°C
|
ISO 11359-2
|
|
电气性能
|
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+15
|
ohms
|
IEC 60093
|
|
体积电阻率
|
> 1.0E+15
|
ohms·cm
|
IEC 60093
|
|
介电常数 (100 Hz)
|
2.50
|
|
IEC 60250
|
|
耗散因数
|
|
|
IEC 60250
|
|
100 Hz
|
3.0E-4
|
|
IEC 60250
|
|
1 MHz
|
8.0E-4
|
|
IEC 60250
|
|
漏电起痕指数
|
600
|
V
|
IEC 60112
|
|
光学性能
|
额定值
|
单位制
|
测试方法
|
|
折射率 3
|
1.570
|
|
ASTM D542, ISO 489
|
|
透射率 (550 nm)
|
90.0
|
%
|
ASTM D1003
|
|
雾度
|
1.6
|
%
|
ASTM D1003
|
|
注射
|
额定值
|
单位制
|
|
|
加工（熔体）温度
|
180 到 250
|
°C
|
|
|
模具温度
|
30.0 到 50.0
|
°C
|
|
|
备注
|
|
1 .
|
0% to 85% RH gradient
|
|
2 .
|
标准 B (120°C/h), 压 力1 (10N)
|
|
3 .
|
Sodium D Line
|
...